Solution Description
Textile ceramics are mainly created from alumina ceramic resources, which have excellent complete specialized properties this sort of as higher mechanical power, substantial hardness, low large-frequency dielectric loss, high temperature insulation resistance, chemical resistance and good thermal conductivity.
Substance choice:
Steatite
Alumina up to ninety nine.7 % or ninety five% alumina
Titania
Zirconia
Selection of merchandise:
Flange Eyelet, Double flange eyelet, Slotted eyelet, groove eyelets, step eyelet, Reduce Eyelet, Phase Eyelets, Tubes, Rods, Sleeve,
Ring, Bush, Disc, Dish, Washer, Plates Trap Xihu (West CZPT ) Dis., Traverse Xihu (West CZPT ) Dis., Pig tail Xihu (West CZPT ) Dis., Canine tail Xihu (West CZPT ) Dis., Rollers, Oilers, Oiling Nozzles Cutters
Software :
Yarn production equipment
Tornado machines
Airjet looms
Round looms
weaving devices
winder devices
Rope,Faucet plants
Tailored guides as per thorough drawings and technical specs.
Material information:
|
Merchandise |
Device |
95% al2o3 |
99% al2o3 |
Zirconia |
Black Tio2 |
Yellow Tio2 |
|
Coloration |
|
white,pink |
product,pink |
white,black,yellow |
Black |
Yellow |
|
Density |
g/cm3 |
3.sixty five |
3.nine |
6 |
4 |
four |
|
Flexural toughness |
MPA |
290 |
390 |
1300 |
70 |
70 |
|
Compressive energy |
MPA |
3300 |
3900 |
3000 |
600 |
600 |
|
Vickers hardness |
HV0.5 |
1800 |
2000 |
1150 |
900 |
900 |
|
Thermal growth cofficient |
10-6 K-three |
five-8.3 |
five.4-8.3 |
ten |
8.5 |
8.five |
|
Thermal conductivity |
w/mk |
23 |
28 |
two |
25 |
twenty five |
ep has a vast range of pulleys in inventory and ready to ship. All spare pulleys are produced of substantial-quality aluminum and have pilot holes as standard. Flanges are manufactured of metal zinc sheet if necessary, but you can specify other supplies by custom made order. Stock aluminum pulleys are offered in imperial and metric pitches. We can modify stock pulleys in accordance to your demands. You can make contact with customer service for pricing and shipping.